标准：

 GB T 6609.36-2009 氧化铝化学分析方法和物理性能测定方法 第36部分_ 流动时间的测定标准,用于氧化铝物理性能测定方法设计（流动性能）

standard:

  GB T 6609.36-2009 Alumina chemical analysis method and physical property determination method Part 36_ Flow time measurement standard, used for alumina physical property determination method design (flow property)

技术参数:

漏斗：不锈钢材质，漏斗上口外径138.5mm,内径123mm

出口直径：3.95mm～4.0mm,总高度190.5mm。

上口锥度：60°，下料口锥度15°

Technical Parameters:

Funnel: made of stainless steel, the outer diameter of the top of the funnel is 138.5mm, and the inner diameter is 123mm

Outlet diameter: 3.95mm～4.0mm, total height 190.5mm.

Upper taper: 60°, lower feed taper 15°

试样的制备：

将样品放在一个托盘内，平铺厚度小于5mm，在实验室空气中平衡2h以上。将分析用样品通过试验筛除去大的颗粒，将样品分成3部分，每部分大约105-120g

Preparation of the sample:

Place the sample in a tray with a tile thickness less than 5mm, and equilibrate in the laboratory air for more than 2 hours. Pass the sample for analysis through a test sieve to remove large particles, divide the sample into 3 parts, each about 105-120g

测试步骤:

1.将设备放在无震动的环境中，保证漏斗在稳定的工作台上，且上部表面处于水平

2.对不经常使用的设备，先用适量氧化铝试样通过漏斗来使其达到试验要求。

3.称取100g士0.1g试样，放入到合适的容器内。

4.将漏斗出口堵住，将称好的试料注入漏斗内，将出口阻碍物移去，同时立即记录流动起始时间，试料一旦完全流过漏斗就停止计时。流动过程中绝不能敲打漏斗。

5.从台上取下漏斗，用干布条将漏斗清理干净。将其放进一个密封容器内，以防止出口孔内表面被空气氧化。